Thermo-oxidative resistance of C-rich SiCN(O) nonwovens influenced by the pretreatment of the silazane

Titelangaben

Ramlow, Heloisa ; Ribeiro, Luiz F. B. ; Schafföner, Stefan ; Motz, Günter ; Machado, Ricardo A. F.:
Thermo-oxidative resistance of C-rich SiCN(O) nonwovens influenced by the pretreatment of the silazane.
In: Journal of the European Ceramic Society. Bd. 44 (2024) Heft 9 . - S. 5308-5318.
ISSN 0955-2219
DOI der Verlagsversion: https://doi.org/10.1016/j.jeurceramsoc.2024.01.035

Volltext

	Format: PDF Name: 1-s2.0-S0955221924000347-main.pdf Version: Veröffentlichte Version Verfügbar mit der Lizenz Creative Commons BY-NC-ND 4.0: Namensnennung, nicht kommerziell, keine Bearbeitung
	Download (8MB)

Abstract

C-rich SiCN(O) ceramic nonwovens with thermo-oxidation resistance up to 600 °C were developed from electrospinning of polyacrylonitrile in combination with different ratios of an oligomeric or polymeric silazane and subsequent pyrolysis. The influence of the selective pre-polymerization of the oligosilazane and the respective amount on the electrospinning, pyrolysis, phase formation and the properties of the resulting C-rich ceramic nonwovens was evaluated. The fiber diameter after pyrolysis at 1000 °C ranges from 0.26 to 0.63 µm. The oligosilazane/PAN-derived ceramic nonwovens contain high oxygen and carbon content because of high reactivity leading to a high ceramic yield due to additional crosslinking. A higher initial oxidation temperature compared to pure carbon was confirmed for all samples. However, the best result was achieved with a sample based on a high proportion of polysilazane in combination with PAN, as a dense passivating layer to protect the free carbon regions was obviously better able to form.