Synthesis, Superstructure, Vacancy-Ordering of Intercalated Transition Metal Dichalcogenides

Titelangaben

Ali, Sk Imran:
Synthesis, Superstructure, Vacancy-Ordering of Intercalated Transition Metal Dichalcogenides.
Bayreuth , 2014 . - 2, VI, 110 S.
( Dissertation, 2014 , Universität Bayreuth, Fakultät für Mathematik, Physik und Informatik)

Volltext

	Format: PDF Name: imran_dissertation_lab_crystallography_vansmaalen.pdf Version: Veröffentlichte Version Verfügbar mit der Lizenz Creative Commons BY 3.0: Namensnennung
	Download (20MB)

Abstract

In this thesis, the synthesis and crystal structures are discussed of intercalated transition metal dichalcogenides (TMDCs) 6R-CuxTa1+yS2 and 2H-CuxTa1+ySe2, as well as the compound Cu3TaSe4. Synthesis of these compounds has been performed by the method of chemical vapor transport, using iodine as a transporting agent. X-ray diffraction may reveal superlattice reflections, which then indicates the existence of a superstructure. An eightfold superstructure has been found for 6R-CuxTa1+yS2 (x = 0.237, y = 0; x = 0.23, y = 0.06) and a fourfold superstructure has been found for 2H-Cu0:52TaSe2. 2H-Cu0:16Ta1:08Se2 and Cu3TaSe4 do not form any superstructure.

Abstract in weiterer Sprache

In dieser Arbeit wurden die Synthesen und Kristallstrukturen von Übergangsmetalldichalkogenide (engl.: Transition Metal Dichalcogenides, TMDCs) 6R-CuxTa1+yS2 and 2H-CuxTa1+ySe2, sowie von der Verbindung Cu3TaSe4 untersucht. Die Synthese dieser Verbindungen wurde mit Hilfe des chemischen Transports (engl.: chemical vapor transport, CVT) durchgef¨uhrt, wobei Jod als Transportmittel diente. Bei der Röntgenbeugung können Überstrukturreflexe auftreten, was auf die Existenz einer Überstruktur hinweist. Für 6R-CuxTa1+yS2 (x = 0.237, y = 0; x = 0.23, y = 0.06) wurde eine achtfache Überstruktur und für 2H-Cu0:52TaSe2 wurde eine vierfache Überstruktur gefunden. 2H-Cu0:16Ta1:08Se2 und Cu3TaSe4 bilden keine Überstrukturen.