Mechanical Properties of Strand PET Foams at Different Length Scales

DOI zum Zitieren dieses Dokuments: https://doi.org/10.15495/EPub_UBT_00004286
URN to cite this document: urn:nbn:de:bvb:703-epub-4286-9

Title data

Fathi, Amir:
Mechanical Properties of Strand PET Foams at Different Length Scales.
Bayreuth , 2018 . - 158 P.
( Doctoral thesis, 2018 , University of Bayreuth, Faculty of Engineering Science)
DOI: https://doi.org/10.15495/EPub_UBT_00004286

[img] PDF
190304_Dissertation_Amir Fathi.pdf - Published Version
Available under License Creative Commons BY 4.0: Attribution .

Download (16MB)

Abstract

Kunststoff-Hartschäume weisen einen breiten Einsatz in strukturellen Anwendungen auf. Das mechanische Verhalten von Schäumen wird durch das Eigenschaftsprofil des jeweiligen Basismaterials sowie die Dichte und Morphologie der Zellstruktur des Schaumes bestimmt [1]. Hiervon haben das Basismaterial und die Schaumdichte den größten Einfluss auf die mechanischen Eigenschaften. Daneben kann auch die Zellmorphologie einen erheblichen Einfluss auf die makroskopischen Eigenschaften des Schaumes haben. Das Verständnis des komplexen Zusammenspiels von Zellmorphologie, Zelldeformation und resultierenden mechanischen Eigenschaften des Schaumes ermöglichen zukünftig Schäume mit gezielt verbessertem Eigenschafts-Gewichts-Verhältnis. In der vorliegenden Arbeit werden Struktur-Eigenschafts-Beziehungen von PET-Schäumen (Strand PET Foams) in einem Dichtebereich von 80 bis 200 kg/m³ aufgestellt. Extrudierte PET-Schäume können als eine geschäumte Honigwabenstruktur, gefüllt mit Schaum beschrieben werden. Es wird gezeigt, dass diese Schäume eine zu Holz sehr ähnliche Morphologie aufweisen, da einige Zellen sehr ausgeprägte Dehnungen und Orientierungen in Richtung der Plattendicke aufweisen. Die Kombination der holzähnlichen Mikrostruktur mit der einer Honigwabe führt zu einem deutlich anisotropem mechanischen Verhalten. Für eine quantifizierte Analyse des Morphologieeinflusses wird das Verhalten der Hartschäume unter Druckbelastung auf verschiedenen Längenskalen analysiert und diskutiert. Darauf aufbauend werden durch optische Messungen Vollfeld-Verformungsmuster mit den lokalen Zelldeformationsmechanismen korreliert. Es konnten hierbei zwei fundamental-unterschiedliche Deformationsmechanismen identifiziert werden. Bei einer Belastung orthogonal zur Schaumplatte erfolgt eine starke axiale Deformationsantwort der ineinander verhakten und gedehnten Zellen, gefolgt von einem lokalen, plastischen Knicken der Zellwände. Im Gegensatz hierzu zeigt sich bei einer Belastung in Plattenebene eine plastische Deformation der Zellwände und -stege. Die Deformation unter Belastung in Richtung der Plattenebene erwies sich als geordnet und regelmäßig mit geometrischen Ähnlichkeiten zu einer hexagonalen Form. Auch unterschiedliche Deformationsmechanismen auf Zellebene (Knicken oder Biegen) zeigen unterschiedliche, charakteristische Verläufe in den Druckspannungs-Stauchungs-Kurven. In einem weiteren Schritt wurden die zuvor ermittelten Korrelationen für unterschiedliche Schaumdichten überprüft. Hierdurch wird im Rahmen eines völlig anderen experimentellen Versuchsaufbaus bestätigt, dass die Zelldeformation bei Belastung senkrecht zur Bauteilebene dehnungsdominiert (stretch-dominated) erfolgt und bei einer Belastung in Plattenebene eher eine biegungsdominierte Deformation der Zellen vorliegt (bending-dominated). Die Versuchsergebnisse der Dichtevariationsstudie sowie der in-situ Deformationsmessungen stehen demnach in Einklang und bestätigen die zugrundeliegende Hypothese. Ebenso wurde aufgezeigt, dass bei PET-Schäumen mit hoher Dichte (200 kg/m³) die gemessenen mechanischen Eigenschaften unterhalb derer liegen, die bei Anwendung der Dichteskalierung zu erwarten wären. Die Reduzierung des Zellenaspektverhältnisses bei hohen Dichten bewirkt einen veränderten Deformationsmechanismus, wodurch es zu einer Abweichung der Versuchsergebnisse von den theoretisch zu erwartenden mechanischen Eigenschaften kommt.

Abstract in another language

Rigid polymer foams are used in a broad range of structural applications. The mechanical behavior of foams is governed by the properties of the base material, the relative foam density (ρ), and the morphological features of the cellular structure [1]. Clearly, the first two, namely material type and relative density, have the highest impact on the mechanical properties. Nevertheless, the cellular morphology, too, can have a strong influence on the resulting macroscopic properties. Foams with complex cell morphologies usually have anisotropic mechanical responses. Understanding the relations between cell morphology, cell deformation mechanisms, and the mechanical properties in such foams will enable future foam generations with even better performance to weight ratios. In the present thesis, structure-properties correlations at different length scales are established for strand PET foam in a density range of 80 to 200 kg/m³. Strand PET foam can be described as a foamed honeycomb, filled with foam. It is shown that the cell morphology of strand PET foam has huge analogies to that of wood, since a fraction of cells are highly elongated and oriented through the panel thickness. The combination of both honeycomb- and wood-like morphology results in strong anisotropy in mechanical properties. Following quantitative morphology analysis, the multi-scale compression response of strand PET foam (T92.100) is identified and discussed. The full-field crush patterns of the foam specimens were correlated to the local cell deformation mechanisms. Two fundamentally different cell deformation mechanisms were observed. When loaded in the out-of-plane direction, the interlocked elongated cells activate a strong axial deformation response, followed by local plastic buckling of the cell walls. This behavior was manifested as several irregular shear bands throughout the specimen thickness. On the contrary, the cell deformation mechanism in the in-plane loading direction is governed by a weaker plastic bending of the cell walls and struts. The full-field deformation maps in the in-plane loading were orderly and regular, with geometrical similarities to hexagonal shapes. A two-stage plastic yielding of the foam cells located in different strand regions caused this regularity in strain fields. Different cell level deformation mechanisms (buckling or bending) also left distinct signatures on the global stress-strain curves. For example, the axial deformation and buckling of the elongated foam cells cause a post-yield softening response in the out-of-plane stress-strain curve. In the next step, the findings are extended to other foam densities. The fitted curves to the property-density data had different slopes for the out-of-plane and in-plane loading directions. This also confirmed, from a completely different experimental approach, that the cell deformation mechanisms in the out-of-plane and in-plane loadings are stretch-dominated and bending-dominated, respectively. The findings from both density-scaling approach and the in-situ deformation measurements agreed well and verified the hypotheses. Last but not least, it is demonstrated that in the high density PET foam (200 kg/m³), the measured mechanical properties are lower than the predicted values using the density scaling laws. The reduction of cell aspect ratio at this density creates a shift in the deformation mechanism. This makes the macroscopic measurements deviate from the theoretical predictions.

Further data

Item Type: Doctoral thesis (No information)
Keywords: Polymer Foams; Strand Foams; PET Foams; Compression properties; Anisotropy; Cell morphology; Digital Image Correlation (DIC)
DDC Subjects: 500 Science
500 Science > 540 Chemistry
600 Technology, medicine, applied sciences
600 Technology, medicine, applied sciences > 620 Engineering
600 Technology, medicine, applied sciences > 670 Manufacturing
600 Technology, medicine, applied sciences > 680 Manufacture for specific uses
Institutions of the University: Faculties > Faculty of Engineering Science
Faculties > Faculty of Engineering Science > Chair Polymer Engineering
Faculties > Faculty of Engineering Science > Chair Polymer Engineering > Chair Polymer Engineering - Univ.-Prof. Dr.-Ing. Volker Altstädt
Faculties > Faculty of Engineering Science > Chair Engineering Design and CAD
Faculties > Faculty of Engineering Science > Chair Engineering Design and CAD > Chair Engineering Design and CAD - Univ.-Prof. Dr.-Ing. Frank Rieg
Faculties
Language: English
Originates at UBT: Yes
URN: urn:nbn:de:bvb:703-epub-4286-9
Date Deposited: 16 Apr 2019 08:27
Last Modified: 13 May 2019 08:00
URI: https://epub.uni-bayreuth.de/id/eprint/4286

Downloads

Downloads per month over past year