Strengthening Potentials of Lithium-Doped Soda-Lime-Silicate Glasses Through Surface Crystallization of Quartz-ss

Titelangaben

Stoelzel, Fabian ; Gerdes, Thorsten:
Strengthening Potentials of Lithium-Doped Soda-Lime-Silicate Glasses Through Surface Crystallization of Quartz-ss.
In: International Journal of Applied Glass Science. Bd. 17 (2026) Heft 2 . - e70023.
ISSN 2041-1294
DOI der Verlagsversion: https://doi.org/10.1111/ijag.70023

Volltext

	Format: PDF Name: Int J of Appl Glass Sci - 2026 - Stoelzel - Strengthening Potentials of Lithium‐Doped Soda Lime Silicate Glasses Through.pdf Version: Veröffentlichte Version Verfügbar mit der Lizenz Creative Commons BY 4.0: Namensnennung
	Download (2MB)

Abstract

The formation of a crystallized surface layer, having a lower coefficient of thermal expansion (CTE) than the parent glass, can be exploited to place the glass surface under compression during cooling from crystallization temperature and hence improve mechanical properties. In our study, we focused on the understanding of the compositional dependency of the surface crystallization of quartz solid solutions (Qz-ss) with potentially low CTE. Specifically, we investigated the crystallization of melt-prepared soda–lime–silicate glasses with variable Al2O3 content that were doped with lithium in exchange for sodium. Further, the role of ZnO and MgO in the crystallization was evaluated. Despite rather complex glass compositions, the observed cell parameters of the obtained Qz-ss are close to the corresponding ternary Li2O─Al2O3─SiO2 (LAS) system. Further, a simple model was applied to predict the in-plane stresses in the surface. For modeled compositions down to 5.5 mol% Al2O3, formation of a compressive layer for the complete range of the crystalline content can be observed. Our findings illustrate the potential of strengthening glasses through surface crystallization as an alternative to thermal- and chemical strengthening to make glass-packaging more weight competitive. The results can help to optimize glass compositions that can be strengthened by this method.