Ausrichtung von Blockcopolymerfilmen im Elektrischen Feld: Eine In-Situ Rasterkraftmikroskopische Untersuchung

URN to cite this document: urn:nbn:de:bvb:703-opus-4099

Title data

Olszowka, Violetta:
Ausrichtung von Blockcopolymerfilmen im Elektrischen Feld: Eine In-Situ Rasterkraftmikroskopische Untersuchung.
Bayreuth , 2007
( Doctoral thesis, 2008 , University of Bayreuth, Faculty of Biology, Chemistry and Earth Sciences)

	Format: PDF Name: Dissertation.pdf Version: Published Version Available under License Creative Commons BY 3.0: Attribution
	Download (22MB)
	Format: Archive (ZIP) Name: Filme.zip Version: Published Version Available under License Creative Commons BY 3.0: Attribution
	Download (31MB)

Abstract

Im Rahmen dieser Arbeit wurde die Reorientierung sowohl von dünnen als auch dicken Diblockcopolymerfilmen mit lamellarer Mikrodomänenstruktur im realen Raum untersucht. Die Experimente erfolgten unter Tempern im Lösungsmitteldampf im planaren elektrischen Feld. Es wurden zwei Wege gezeigt, wie lamellare Mikrodomänen aufgestellt und durch ein elektrisches Feld in drei Dimensionen ausgerichtet werden können. In beiden Fällen wurden periodische und hochgeordnete Streifenstrukturen erhalten. Sowohl der Reorientierungsmechanismus der Mikrodomänen als auch der Einfluss des elektrischen Feldes auf die Defektbeweglichkeiten im dünnen Film, wurden mit einem modifizierten AFM, dem so genannten quasi in-situ AFM untersucht. Der Mechanismus der Reorientierung im dicken Film wurde durch eine kombinierte Studie aus AFM, GISAXS, REM und in-situ Ellipsometrie ermittelt. Weiterhin wurden der Verlauf der elektrischen Feldlinien und die Feldstärke für die verwendete Elektrodengeometrie auf der Basis der Finiten-Elemente-Methode simuliert. Ferner wurde der Einfluss des elektrischen Feldes auf den Grad der Ausrichtung für die Polymere SHM und SV untersucht. Hierfür wurden kombinatorische Experimente mit Elektroden in Gradientengeometrie durchgeführt.

Abstract in another language

The orientation of thin and thick lamella-forming block copolymers under solvent vapor annealing in the presence of an in-plane electric field has been studied in real space. Two methods have been presented to orient lamellar microdomains both perpendicular to the plane of the film and parallel to the electric field. Highly periodic and ordered upstanding three dimensional structures were obtained in both cases. The orientation mechanism of the microdomains in thin films as well as the influence of the electric field on the defect velocity, were determined with a newly designed quasi in-situ AFM. The orientation mechanism in thick films was studied by a combined AFM, GISAXS, SEM and spectroscopic ellipsometry analysis. The devolution of the electric field lines and the electric field strength were simulated by the finite element method. Furthermore, the dependence of the degree of order of the lamellar microdomains on the electric field strength was studied for the polymers SHM and SV in a combinatorial approach using electrodes with a gradient geometry.

Further data

Item Type:	Doctoral thesis (No information)
Keywords:	Blockcopolymere; Rasterkraftmikroskopie; elektrisches Feld; Orientierung; Lamellen; AFM; block copolymers; lamella; orientation; electric field
DDC Subjects:	500 Science > 540 Chemistry
Institutions of the University:	Faculties > Faculty of Biology, Chemistry and Earth Sciences > Department of Chemistry Faculties Faculties > Faculty of Biology, Chemistry and Earth Sciences
Language:	German
Originates at UBT:	Yes
URN:	urn:nbn:de:bvb:703-opus-4099
Date Deposited:	25 Apr 2014 11:21
Last Modified:	25 Apr 2014 11:23
URI:	https://epub.uni-bayreuth.de/id/eprint/647

Download Statistics

Download Statistics

Download Statistics

Downloads

Downloads per month over past year